The fabrication of polymeric composite hydrogel with hierarchical structure in a simple, controllable, and straightforward process poses great importance for manufacturing nanomaterials and subsequent applications. Herein, we report a one-step and template-free counterion exchange method to construct free-standing carboxylated cellulose nanofiber composite hydrogels. Metal ions were electrochemically and locally released from the electrode and chelated with carboxylated cellulose nanofibers, leading to the in-situ formation of composite hydrogels. The properties of composite hydrogels can be easily programmed by the type of electrode, current density, and electrodeposited suspension. Significantly, the composited hydrogels exhibited interconnected nanoporous structure, enhanced thermal degradation, improved mechanical strength and antibacterial activity. https://www.selleckchem.com/products/lb-100.html The results suggest great potential of anodic electrodeposition to fabricate nanofiber/metal composite hydrogels.Better understanding through direct observation of the mechanisms involved in chemical and enzymatic hydrolysis of biomass is of great importance, to implement a substitute for the common cellulose standards. We report the hydrolysis of biomass, using exclusively the parenchyma, to isolate cellulose nanoplatelets using a less harsh pretreatment. Then, we show direct evidence of the effect of endoglucanase on the structure of cellulose nanoplatelets, finding that amorphous cellulose is exclusively digested, loosening the cellulose nanofibrils in the process. The analysis of micrographs demonstrates that when cellulose nanoplatelets are deposited on a silicon wafer, its thickness can be qualitatively measured by the interference color detected using an optical microscope. This finding facilitates further studies of mechanisms involved in lignin removal and cellulose nanofibrils production by specific enzymatic digestion.A neutral branched heteropolysaccharide (Pc0-1) was purified from the spores of Paecilomyces cicadae, which parasitized in the bamboo cicada (Platylomia pieli Kato). The structure of Pc0-1 was analyzed by HPLC, IR, methylation and NMR spectroscopy. The results reveal that Pc0-1, with an average molecular weight of 18 × 103 kDa, consists of glucose, galactose, mannose and arabinose in the molar ratio of 8541. Some of the glucose residues have methyl modification at O-6 position. The Pc0-1 polysaccharide has a core structure containing 1,2-linked α-d-Manp residues as the backbone and branches at the O-3 and O-6 of the α-d-Manp residues. The inner part of the side-chains is comprised of 1,4-linked α-d-Glcp and 1,4-linked 6-O-Me-α-d-Glcp residues. 1,2-linked β-Galf and minor 1,4-linked Arap and 1,3 or 4-linked Arap residues were occasionally linked at the outside of the side-chains. The side-chains have a single terminal residue of α-d-Glcp, α-Manp, β-Galf or minor Arap (minor). Studies on the bioactivity of Pc0-1 on the macrophages show it exhibit moderate immunostimulating activity through increasing the production of nitric oxide (NO) and enhancing the secretion of major inflammatory cytokines by macrophages, such as TNF-α, IL-1β, IL-6, in RAW 264.7 cells. We examined the effect of Pc0-1 on induced NO and cytokine production in macrophages using anti-PRR antibodies to investigate the membrane receptor for the polysaccharide. The results show that Pc0-1 mainly activates macrophages through their mannose receptor (MR). TLR4 and TLR2 also participated in the recognition of Pc0-1.In the work, the non-woven cellulose acetate (CA) nanofiber mats were prepared via electrospinning, and CA nanofiber were incorporated into the core layer of the high-pressure laminates (HPLs). When the concentration of CA was 16 wt%, SEM images demonstrated that the morphology of the CA nanofiber mat was the best, with an average diameter of 654±246 nm. When CA nanofiber mats were incorporated into the core layer of HPLs, the mechanical properties of the resulted HPLs composites were significantly improved. Specifically, the tensile strength and elongation at break of the nanofiber mats reinforced HPLs composites increased remarkably to 40.8 ±1.1 MPa and 27.9 ± 0.9 %, respectively, which were nearly 6 times and 4.4 times higher than those of the pure HPLs. Furthermore, the incorporation of the CA nanofiber mats also significantly improved the flame retardancy of the HPLs, which was revealed from the thermogravimetric analysis (TGA) results.We propose a new methodology for direct evaluation of the degree of fibrillation of fibrillating pulp suspensions through the pixel-resolved retardation distribution. Through simple normalization by just injecting a pulp suspension with a certain concentration into a quartz flow channel with a constant cross-sectional shape, the degree of fibrillation (i.e., the degree of bundling of cellulose molecular chains) can be directly mapped by the retardation gradation, reflecting locally high retardation (pulp fibers), smaller retardation (balloons on fibrillating pulps), and much smaller retardation close to water (dispersed nanofibers). Both the average retardation and standard deviation are found to be the direct indicators of the degree of fibrillation. We envision that the proposed methodology will become the future standard for determining the degree of fibrillation by the retardation distribution, and it will pave the way for more precise control of pulp fibrillation and more sophisticated applications of cellulose nanofiber suspensions.As a major therapeutic approach for cancer treatment, the effectiveness of chemotherapy is challenged by multidrug resistance (MDR). Herein, we fabricated novel redox-responsive, chondroitin sulfate-based nanoparticles that could simultaneously deliver quercetin (chemosensitizer), chlorin e6 (photosensitizer) and paclitaxel (chemotherapeutic agent) to exert enhanced chemo-photodynamic therapy for overcoming MDR and lung metastasis of breast cancer. In vitro cell study showed that nanoparticles down-regulated the expression of P-glycolprotein (P-gp) on MCF-7/ADR cells and thereby improved the anticancer efficacy of PTX against MCF-7/ADR cells. Moreover, NIR laser irradiation could induce nanoparticles to generate cellular reactive oxygen species (ROS), leading to mitochondrial membrane potential loss, and meanwhile facilitating lysosomal escape of drugs. Importantly, the novel nanoplatform exhibited effective in vivo MDR inhibition and anti-metastasis efficacy through enhanced chemo-photodynamic therapy. Thus, the study suggested that the multifunctional nanoplatform had good application prospect for effective breast cancer therapy.